TORICH GB / T 24187 Kaltgezogene Präzisions-Einzelschweißstahlrohre
Spezifikation :
Material: C Si Mn PS
Größenbereich : OD: 3.18-18mm
WT: 0,3-1,3 mm
Allgemeine Länge: 1,5-4m
Toleranz:
Nach den folgenden Tabellen oder Kundenwunsch.
Tabelle 1 Außendurchmesser, Wanddicke und theoretisches Gewicht
|
OD/mm
|
WT/mm
|
|
0.30
|
0.40
|
0.50
|
0.60
|
0.65
|
0.70
|
0.80
|
0.90
|
1.00
|
1.30
|
|
theoretical weight /(kg/m)
|
|
3.18
|
0.0213
|
0.0274
|
0.0330
|
|
|
|
|
|
|
|
|
4.00
|
0.0274
|
0.0355
|
0.0432
|
0.0503
|
|
|
|
|
|
|
|
4.76
|
0.0330
|
0.0430
|
0.0525
|
0.0616
|
0.0659
|
0.0701
|
|
|
|
|
|
5.00
|
0.0348
|
0.0454
|
0.0555
|
0.0651
|
0.0697
|
0.0742
|
|
|
|
|
|
6.00
|
0.0422
|
0.0552
|
0.0678
|
0.0799
|
0.0858
|
0.0915
|
0.1026
|
0.1132
|
0.1233
|
|
|
6.35
|
0.0448
|
0.0587
|
0.0721
|
0.0851
|
0.0914
|
0.0975
|
0.1095
|
0.1210
|
0.1319
|
|
|
7.94
|
0.0565
|
0.0744
|
0.0917
|
0.1086
|
0.1169
|
0.1250
|
0.1409
|
0.1563
|
0.1712
|
0.2129
|
|
8.00
|
0.0570
|
0.0750
|
0.0925
|
0.1095
|
0.1178
|
0.1260
|
0.1421
|
0.1576
|
0.1726
|
0.2148
|
|
9.53
|
0.0683
|
0.0901
|
0.1113
|
0.1321
|
0.1423
|
0.1524
|
0.1722
|
0.1915
|
0.2104
|
0.2639
|
|
10.00
|
0.0718
|
0.0947
|
0.1171
|
0.1391
|
0.1499
|
0.1605
|
0.1815
|
0.2020
|
0.2220
|
0.2789
|
|
12.00
|
0.0866
|
0.1144
|
0.1418
|
0.1687
|
0.1819
|
0.1951
|
0.2210
|
0.2464
|
0.2713
|
0.3430
|
|
12.70
|
0.0917
|
0.1213
|
0.1504
|
0.1790
|
0.1932
|
0.2072
|
0.2348
|
0.2619
|
0.2885
|
0.3655
|
|
14.00
|
0.1014
|
0.1342
|
0.1665
|
0.1983
|
0.2140
|
0.2296
|
0.2604
|
0.2908
|
0.3206
|
0.4072
|
|
15.88
|
0.1153
|
0.1527
|
0.1896
|
0.2261
|
0.2441
|
0.2621
|
0.2975
|
0.3325
|
0.3670
|
0.4674
|
|
16.00
|
0.1162
|
0.1539
|
0.1911
|
0.2279
|
0.2461
|
0.2641
|
0.3000
|
0.3352
|
0.3699
|
0.4713
|
|
18.00
|
0.1310
|
0.1736
|
0.2158
|
0.2575
|
0.2781
|
0.2987
|
0.3393
|
0.3795
|
0.4192
|
0.5354
|
Theoretical weight of no additional coating, density of steel is 7.85 kg/
|
Tabelle2 Zulässige Abweichung des Außendurchmessers des Stahlrohrs
|
Outer diameter
|
Common precision
|
High precision
|
|
＜4.76
|
±0.08
|
±0.05
|
|
4.76-8.00
|
±0.12
|
±0.07
|
|
＞8.00-12.00
|
±0.16
|
±0.10
|
|
＞12.00
|
±0.20
|
±0.12
|
Tabelle 3 Zulässige Abweichung der Stahlrohrwanddicke
|
Wall thickness
|
Permissible deviation
|
|
＜0.70
|
±0.05
|
|
≥0.70
|
±0.07
|
Tabelle 4 Zulässige Abweichung der spezifizierten Länge des Stahlrohrs
|
Length
|
Allowable deviation
|
|
≤2000
|
+4
0
|
|
＞2000-5000
|
+7
0
|
|
＞5000-8000
|
+10
0
|
Tabelle 5 Chemische Zusammensetzung des Stahlbandes (Massenanteil)%
|
Category
|
C
|
Si
|
Mn
|
P
|
S
|
|
Cold rolled low carbon steel strip
|
≤0.08
|
≤0.03
|
≤0.30
|
≤0.030
|
≤0.030
|
|
Cold rolled ultra low carbon steel strip
|
≤0.008
|
≤0.03
|
≤0.25
|
≤0.020
|
≤0.030
|
Tabelle 6 Mechanische Eigenschaften von kaltgewalztem kohlenstoffarmem Stahlband
|
Thickness
/mm
|
Tensile Strength
|
Yield Strength
|
Elongation
A/%
|
|
0.25~＜0.35
|
≥270
|
|
≥32
|
|
0.35~＜0.50
|
≥34
|
|
≥0.50
|
≥36
|
|
a Replace with  when the yield phenomenon is not obvious.
b Sample type of sample number D14 in GB/T 228-2002.
|
Tabelle 7 Mechanische Eigenschaften von kaltgewalztem Stahlband mit extrem niedrigem Kohlenstoffgehalt
|
Thickness
/mm
|
Tensile Strength
|
Yield Strength
|
Elongation
A/%
|
|
≤0.50
|
≥280
|
130~250
|
≥38
|
|
＞0.50
|
≥40
|
|
a Replace with when the yield phenomenon is not obvious.
b Sample type of sample number P14 in GB/T 228-2002.
|
Tabelle 8 Mechanische Eigenschaften von Stahlrohren
|
Category
|
Tensile Strength
|
Yield Strength
|
Elongation
A/%
|
|
Ordinary steel pipe(MA)
|
≥270
|
≥180
|
≥14
|
|
Soft steel tube(MB)
|
≥230
|
150~220
|
≥35
|
|
a Replace with when the yield phenomenon is not obvious.
b Sample type of sample number S7 in GB/T 228-2002.
|
Charakteristisch:
TORICH QUALITÄTSSICHERUNG
Gute Oberflächenqualität
Gute OD- und ID-Toleranz gemäß Technischem Standard
Stabile Qualität
100% Wirbelstromprüfung
Verarbeitung: WH WC
Weit verbreitet auf dem Gebiet der: Kondensator, Verdampfer, Kühlerrohr Kraftstoffrohr der Kälte-, Automobil-und Elektrogerät Industrie
Produktbilder :
QUALITÄTSKONTROLLE
1 ~ Eingangskontrolle des Rohmaterials
2 ~ Rohstofftrennung zur Vermeidung von Verwechslungen in Stahlsorten
3 ~ Erhitzen und Hämmern Ende für Kaltzeichnen
4 ~ Kaltziehen und Kaltwalzen, Online-Inspektion
5 ~ Wärmebehandlung, + A, + SRA, + LC, + N, Q + T
6 ~ Richten-Schneiden auf spezifizierte Länge-Fertige messende Inspektion
7 ~ Mechanische Tests in eigenen Labors mit Zugfestigkeit, Streckgrenze, Dehnung, Härte, Schlag, Mictrostruture etc
8 ~ Verpackung und Lagerung.
100% unserer Stahlrohre sind maßgeprüft
100% unserer Stahlrohre werden visuell überprüft, um sicherzustellen, dass sie einen perfekten Oberflächenzustand und keine Oberflächenfehler aufweisen.
100% Wirbelstromprüfung und Ultraschallprüfung zur Beseitigung von longitudinalen und transversalen Defekten.
FAQ
F: handeln Sie Firma oder Hersteller?
A: Ein professioneller Stahlrohrhersteller, Hersteller und Lösungsanbieter
Q: wie lange ist ihre lieferzeit?
A: Im Allgemeinen ist es 7-14 Tage, wenn die Waren auf Lager sind. oder es ist 30-60 tage, wenn die waren nicht auf lager, und es ist nach menge.
Q: Liefern Sie Proben? ist es kostenlos oder extra?
A: Ja, wir könnten das Beispiel für freie Gebühr anbieten, aber Sie müssen die Frachtkosten bezahlen.
F: Was sind Ihre Zahlungsbedingungen?
A: Zahlung <= 1000 USD, 100% im Voraus. Zahlung> = 1000 USD, 30% T / T im voraus, balance vor shippment.
Wenn Sie eine andere Frage haben, zögern Sie nicht uns zu kontaktieren
Contact Now