Modell: ASTM A213
Marke: ZU REICH
Verpakung: In Bündeln In Holzkisten
Produktivität: 60000 Tons per Year
Transport: Ocean,Land,Air
Ort Von Zukunft: China
Unterstützung über: 60000 Tons per Year
Zertifikate : ISO 9001 ISO 14001 TS 16949 EN 10204.3.1 LR KR
HS-Code: 7304419000
Hafen: Ningbo,Shanghai
Zahlungsart: L/C,T/T,D/P,Paypal,Money Gram,Western Union
Incoterm: FOB,CFR,FCA,CPT
Gebrannter, nahtloser Stahlkessel aus Edelstahl
Product Name | ASTM A213 316Ti stainless steel seamless tube |
Material | stainless steel 316Ti |
Process | cold drawn, cold rolling |
Standard | A213, A312, A269, A511 |
Grade | 304, 304L, 316L, 321, 347H, S31803, 904L |
Size | 6 - 610 mm |
Length | 800mm - 20000 mm |
Used | bolier, heat exchanger |
Toleranz für nahtloses Edelstahlkesselrohr:
Production Method | Size(mm) | Tolerance | |
Hot Rolling(Extrusion) | OD | ≤140 | ±1.25% |
>140 | ±1.0% | ||
WT | ≤10 | ±12.5% | |
>10 | ±15% | ||
Cold Drawn(Cold Rolled) | OD | 8~30 | ±0.20mm |
>30~50 | ±0.30mm | ||
>50 | ±0.8% | ||
WT | 1.0~3 |
+12% -10% |
|
>3.0 |
±10% |
Standard | ASME SA213/ASTM A213, ASTM A269/ASME SA269, ASME SA312/ASTM A312, ASME249/ASTM A249, ASME SA511/ASTM A511, ASTM A270/ASME SA270, EN10216-5,EN10305-1, EN10217-5, DIN 17175, DIN 2448, DIN 6258, GOST 8731, JIS G3463, JIS G3462, JIS G3455, JIS G3459 etc. |
Material | TP304, TP304L, TP304H, TP304LN, TP314, TP316, TP316L, TP316LN, TP321, TP321H, TP310, TP310S, TP317, TP317L, TP347, TP347H, N08904, 904l, 253MA(S30815), 254SMO(S31254). |
Type | Seamless / SML |
O.D | 6-530mm |
W.T | 0.7-50mm |
Length | 0-38000mm |
Technique | Cold Finished (Cold Drawing and Cold Rolling), Hot Finished (Hot Extrusion) |
Ends | PE/Plain Ends, BE/Beveled Ends |
Zusammensetzungsbereiche für Edelstahl der Güteklasse 316 .
Grade |
|
C | Mn | Si | P | S | Cr | Mo | Ni | N |
---|---|---|---|---|---|---|---|---|---|---|
316 | Min | - | - | - | 0 | - | 16.0 | 2.00 | 10.0 | - |
Max | 0.08 | 2.0 | 0.75 | 0.045 | 0.03 | 18.0 | 3.00 | 14.0 | 0.10 | |
316L | Min | - | - | - | - | - | 16.0 | 2.00 | 10.0 | - |
Max | 0.03 | 2.0 | 0.75 | 0.045 | 0.03 | 18.0 | 3.00 | 14.0 | 0.10 | |
316H | Min | 0.04 | 0.04 | 0 | - | - | 16.0 | 2.00 | 10.0 | - |
max | 0.10 | 0.10 | 0.75 | 0.045 | 0.03 | 18.0 | 3.00 | 14.0 | - |
Mechanische Eigenschaften von Edelstahl der Güteklasse 316.
Grade | Tensile Str (MPa) min | Yield Str 0.2% Proof (MPa) min | Elong (% in 50 mm) min | Hardness | |
---|---|---|---|---|---|
Rockwell B (HR B) max | Brinell (HB) max | ||||
316 | 515 | 205 | 40 | 95 | 217 |
316L | 485 | 170 | 40 | 95 | 217 |
316H | 515 | 205 | 40 | 95 | 217 |
Typische physikalische Eigenschaften für Edelstahl der Güteklasse 316 .
Grade | Density(kg/m3) | Elastic Modulus (GPa) | Mean Co-eff of Thermal Expansion (µm/m/°C) | Thermal Conductivity (W/m.K) | Specific Heat 0-100 °C (J/kg.K) | Elec Resistivity (nΩ.m) | |||
---|---|---|---|---|---|---|---|---|---|
0-100 °C | 0-315 °C | 0-538 °C | At 100 °C | At 500 °C | |||||
316/L/H | 8000 | 193 | 15.9 | 16.2 | 17.5 | 16.3 | 21.5 | 500 | 740 |
Güteklassen für Edelstahl der Güteklasse 316 .
Grade | UNS No | Old British | Euronorm | Swedish SS | Japanese JIS | ||
---|---|---|---|---|---|---|---|
BS | En | No | Name | ||||
316 | S31600 | 316S31 | 58H, 58J | 1.4401 | X5CrNiMo17-12-2 | 2347 | SUS 316 |
316L | S31603 | 316S11 | - | 1.4404 | X2CrNiMo17-12-2 | 2348 | SUS 316L |
316H | S31609 | 316S51 | - | - | - |
Mechanisches Eigentum
Die Wärmebehandlung der longitudinalen mechanischen Eigenschaften von Stahlrohren muss gemäß der Norm erfolgen.
Material |
Tensile strength MPa ≥ |
Yield Strength MPa ≥ |
Elongation % ≥ |
0Cr18Ni9 | 520 | 205 | 35 |
1Cr19Ni9 | 520 | 205 | 35 |
0Cr19Ni10 | 480 | 175 | 35 |
1Cr18Ni9Ti | 550 | 205 | 40 |
0Cr18Ni12Mo2Ti | 530 | 205 | 35 |
0Cr26Ni5Mo2 | 590 | 390 | 18 |
1Cr17 | 410 | 245 | 20 |
00Cr27Mo | 410 | 245 | 20 |
1Cr25Ti | 440 | 245 | 17 |
Härte:
Für die Rohre mit WT ≥ 2 mm sollten Rockwell-Härteprüfungen durchgeführt werden.
Tests der nahtlosen Kesselrohre:
1.biegetest:
Die Rohre sollten den Biegeversuch ablegen, wenn der OD ≤ 22 mm beträgt. Der Biegewinkel beträgt 90 Grad und der Biegeradius beträgt das 6-fache des Außendurchmessers des Stahlrohrs.
2. Hydraulischer Test;
Wirbelstromprüfungen, Ultraschallprüfungen können anstelle von hydraulischen Prüfungen verwendet werden. Bei der Wirbelstromprüfung wurde GB / T 7735-1995 Gr. A sollte gefolgt werden; bei Ultraschallprüfung GB / T 5777-1996 Gr. C8 sollte befolgt werden.
3. Abflachungstest
4. Flanktest
5. Erweitern Sie den Test
Produktgruppe : Nahtlose Stahlrohre
Privacy statement: Your privacy is very important to Us. Our company promises not to disclose your personal information to any external company with out your explicit permission.
Fill in more information so that we can get in touch with you faster
Privacy statement: Your privacy is very important to Us. Our company promises not to disclose your personal information to any external company with out your explicit permission.